Extreme ultraviolet mask blank with multilayer absorber and method of manufacture

ABSTRACT

Extreme ultraviolet (EUV) mask blanks, methods for their manufacture and production systems therefor are disclosed. The EUV mask blanks comprise a multilayer stack of absorber layers on the capping layer, the multilayer stack of absorber layers including a plurality of absorber layer pairs.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. Non-Provisional applicationSer. No. 16/821,444, filed Mar. 17, 2020, which is a continuation ofU.S. Non-Provisional application Ser. No. 15/652,499, filed Jul. 18,2017, which claims the benefit of U.S. Provisional Application No.62/367,388, filed Jul. 27, 2016, to each of which priority is claimedand each of which are incorporated herein by reference in theirentireties.

TECHNICAL FIELD

The present disclosure relates generally to extreme ultravioletlithography, and more particularly extreme ultraviolet mask blanks witha multilayer absorber and methods of manufacture.

BACKGROUND

Extreme ultraviolet (EUV) lithography, also known as soft x-rayprojection lithography, can be used for the manufacture of 0.0135 micronand smaller minimum feature size semiconductor devices. However, extremeultraviolet light, which is generally in the 5 to 100 nanometerwavelength range, is strongly absorbed in virtually all materials. Forthat reason, extreme ultraviolet systems work by reflection rather thanby transmission of light. Through the use of a series of mirrors, orlens elements, and a reflective element, or mask blank, coated with anon-reflective absorber mask pattern, the patterned actinic light isreflected onto a resist-coated semiconductor substrate.

The lens elements and mask blanks of extreme ultraviolet lithographysystems are coated with reflective multilayer coatings of materials suchas molybdenum and silicon. Reflection values of approximately 65% perlens element, or mask blank, have been obtained by using substrates thatare coated with multilayer coatings that strongly reflect light withinan extremely narrow ultraviolet bandpass, for example, 12.5 to 14.5nanometer bandpass for 13.5 nanometer ultraviolet light.

FIG. 1 shows a conventional EUV reflective mask 10, which is formed froman EUV mask blank, which includes a reflective multilayer stack 12 on asubstrate 14, which reflects EUV radiation at unmasked portions by Bragginterference. Masked (non-reflective) areas 16 of the EUV reflectivemask 10 are formed by etching buffer layer 18 and absorbing layer 20.The absorbing layer typically has a thickness in a range of 51 nm to 77nm. A capping layer 22 is formed over the reflective multilayer stack 12and protects the multilayer stack 12 during the etching process. As willbe discussed further below, EUV mask blanks are made of on a low thermalexpansion material substrate coated with multilayers, capping layer andan absorbing layer, which is then etched to provide the masked(non-reflective) areas 16 and reflective areas 24.

The International Technology Roadmap for Semiconductors (ITRS) specifiesa node's overlay requirement as some percentage of a technology'sminimum half-pitch feature size. Due to the impact on image placementand overlay errors inherent in all reflective lithography systems, EUVreflective masks will need to adhere to more precise flatnessspecifications for future production. Additionally, reduction ofthree-dimensional (3D) mask effects is extremely challenging with EUVlithography using EUV reflective masks having a multilayer reflector andan absorber layer. There is a need to provide EUV mask blanks andmethods of making EUV mask blanks used to make EUV reflective masks andmirrors that will enable the reduction of overlay errors and 3D maskeffects.

SUMMARY

One or more embodiments of the disclosure are directed to a method ofmanufacturing an extreme ultraviolet (EUV) mask blank comprisingproviding a substrate; forming a multilayer stack of reflective layerson the substrate, the multilayer stack including a plurality ofreflective layer pairs; forming a capping layer on the multilayer stack;and forming a multilayer stack of absorber layers on the capping layer,the multilayer stack of absorber layers including a plurality ofabsorber layer pairs, each pair comprising two different absorbermaterials having extinction coefficient (k) values that are differentand index of refraction values (n) that are different.

Additional embodiments of the disclosure are directed to an extremeultraviolet (EUV) mask blank comprising a substrate; a multilayer stackon the substrate, stack of reflective layers on the substrate, themultilayer stack including a plurality of reflective layer pairs; acapping layer on the multilayer stack; and a multilayer stack ofabsorber layers on the capping layer, the multilayer stack of absorberlayers including a plurality of absorber layer pairs, each paircomprising two different absorber materials having extinctioncoefficient (k) values that are different and index of refraction values(n) that are different.

Further embodiments of the disclosure are directed to an extremeultraviolet (EUV) mask blank production system comprising a substratehandling vacuum chamber for creating a vacuum; a substrate handlingplatform, in the vacuum, for transporting an ultra-low expansionsubstrate loaded in the substrate handling vacuum chamber; and multiplesub-chambers, accessed by the substrate handling platform, for formingan EUV mask blank including a multilayer stack on the substrate, stackof reflective layers on the substrate, the multilayer stack including aplurality of reflective layer pairs; a capping layer on the multilayerstack; and a multilayer stack of absorber layers on the capping layer,the multilayer stack of absorber layers including a plurality ofabsorber layer pairs, each pair comprising two different absorbermaterials having extinction coefficient (k) values that are differentand index of refraction values (n) that are different.

BRIEF DESCRIPTION OF THE DRAWINGS

So that the manner in which the above recited features of the presentdisclosure can be understood in detail, a more particular description ofthe disclosure, briefly summarized above, may be had by reference toembodiments, some of which are illustrated in the appended drawings. Itis to be noted, however, that the appended drawings illustrate onlytypical embodiments of this disclosure and are therefore not to beconsidered limiting of its scope, for the disclosure may admit to otherequally effective embodiments.

FIG. 1 schematically illustrates a background art EUV reflective maskemploying a conventional absorber;

FIG. 2 schematically illustrates an embodiment of an extreme ultravioletlithography system;

FIG. 3 illustrates an embodiment of an extreme ultraviolet reflectiveelement production system;

FIG. 4 illustrates an embodiment of an extreme ultraviolet reflectiveelement such as an EUV mask blank;

FIG. 5 illustrates an embodiment of an extreme ultraviolet reflectiveelement such as an EUV mask blank;

FIG. 6 is a reflectivity curve for a mask blank;

FIG. 7 is a reflectivity curve for a mask blank; and

FIG. 8 illustrates an embodiment of a physical deposition chamber.

DETAILED DESCRIPTION

Before describing several exemplary embodiments of the disclosure, it isto be understood that the disclosure is not limited to the details ofconstruction or process steps set forth in the following description.The disclosure is capable of other embodiments and of being practiced orbeing carried out in various ways.

The term “horizontal” as used herein is defined as a plane parallel tothe plane or surface of a mask blank, regardless of its orientation. Theterm “vertical” refers to a direction perpendicular to the horizontal asjust defined. Terms, such as “above”, “below”, “bottom”, “top”, “side”(as in “sidewall”), “higher”, “lower”, “upper”, “over”, and “under”, aredefined with respect to the horizontal plane, as shown in the figures.

The term “on” indicates that there is direct contact between elements.The term “directly on” indicates that there is direct contact betweenelements with no intervening elements.

As used in this specification and the appended claims, the terms“precursor”, “reactant”, “reactive gas” and the like are usedinterchangeably to refer to any gaseous species that can react with thesubstrate surface.

Those skilled in the art will understand that the use of ordinals suchas “first” and “second” to describe process regions do not imply aspecific location within the processing chamber, or order of exposurewithin the processing chamber.

Referring now to FIG. 2 , an exemplary embodiment of an extremeultraviolet lithography system 100 is shown. The extreme ultravioletlithography system 100 includes an extreme ultraviolet light source 102for producing extreme ultraviolet light 112, a set of reflectiveelements, and a target wafer 110. The reflective elements include acondenser 104, an EUV reflective mask 106, an optical reduction assembly108, a mask blank, a mirror, or a combination thereof.

The extreme ultraviolet light source 102 generates the extremeultraviolet light 112. The extreme ultraviolet light 112 iselectromagnetic radiation having a wavelength in a range of 5 to 50nanometers (nm). For example, the extreme ultraviolet light source 102includes a laser, a laser produced plasma, a discharge produced plasma,a free-electron laser, synchrotron radiation, or a combination thereof.

The extreme ultraviolet light source 102 generates the extremeultraviolet light 112 having a variety of characteristics. The extremeultraviolet light source 102 produces broadband extreme ultravioletradiation over a range of wavelengths. For example, the extremeultraviolet light source 102 generates the extreme ultraviolet light 112having wavelengths ranging from 5 to 50 nm.

In one or more embodiments, the extreme ultraviolet light source 102produces the extreme ultraviolet light 112 having a narrow bandwidth.For example, the extreme ultraviolet light source 102 generates theextreme ultraviolet light 112 at 13.5 nm. The center of the wavelengthpeak is 13.5 nm.

The condenser 104 is an optical unit for reflecting and focusing theextreme ultraviolet light 112. The condenser 104 reflects andconcentrates the extreme ultraviolet light 112 from the extremeultraviolet light source 102 to illuminate the EUV reflective mask 106.

Although the condenser 104 is shown as a single element, it isunderstood that the condenser 104 can include one or more reflectiveelements such as concave mirrors, convex mirrors, flat mirrors, or acombination thereof, for reflecting and concentrating the extremeultraviolet light 112. For example, the condenser 104 can be a singleconcave mirror or an optical assembly having convex, concave, and flatoptical elements.

The EUV reflective mask 106 is an extreme ultraviolet reflective elementhaving a mask pattern 114. The EUV reflective mask 106 creates alithographic pattern to form a circuitry layout to be formed on thetarget wafer 110. The EUV reflective mask 106 reflects the extremeultraviolet light 112. The mask pattern 114 defines a portion of acircuitry layout.

The optical reduction assembly 108 is an optical unit for reducing theimage of the mask pattern 114. The reflection of the extreme ultravioletlight 112 from the EUV reflective mask 106 is reduced by the opticalreduction assembly 108 and reflected on to the target wafer 110. Theoptical reduction assembly 108 can include mirrors and other opticalelements to reduce the size of the image of the mask pattern 114. Forexample, the optical reduction assembly 108 can include concave mirrorsfor reflecting and focusing the extreme ultraviolet light 112.

The optical reduction assembly 108 reduces the size of the image of themask pattern 114 on the target wafer 110. For example, the mask pattern114 can be imaged at a 4:1 ratio by the optical reduction assembly 108on the target wafer 110 to form the circuitry represented by the maskpattern 114 on the target wafer 110. The extreme ultraviolet light 112can scan the reflective mask 106 synchronously with the target wafer 110to form the mask pattern 114 on the target wafer 110.

Referring now to FIG. 3 , an embodiment of an extreme ultravioletreflective element production system 200 is shown. The extremeultraviolet reflective element includes a EUV mask blank 204, an extremeultraviolet (EUV) mirror 205, or other reflective element such as an EUVreflective mask 106.

The extreme ultraviolet reflective element production system 200 canproduce mask blanks, mirrors, or other elements that reflect the extremeultraviolet light 112 of FIG. 2 . The extreme ultraviolet reflectiveelement production system 200 fabricates the reflective elements byapplying thin coatings to source substrates 203.

The EUV mask blank 204 is a multilayered structure for forming the EUVreflective mask 106 of FIG. 2 . The EUV mask blank 204 can be formedusing semiconductor fabrication techniques. The EUV reflective mask 106can have the mask pattern 114 of FIG. 2 formed on the mask blank 204 byetching and other processes.

The extreme ultraviolet mirror 205 is a multilayered structurereflective in a range of extreme ultraviolet light. The extremeultraviolet mirror 205 can be formed using semiconductor fabricationtechniques. The EUV mask blank 204 and the extreme ultraviolet mirror205 can be similar structures with respect to the layers formed on eachelement, however the extreme ultraviolet mirror 205 does not have themask pattern 114.

The reflective elements are efficient reflectors of the extremeultraviolet light 112. In an embodiment, the EUV mask blank 204 and theextreme ultraviolet mirror 205 has an extreme ultraviolet reflectivityof greater than 60%. The reflective elements are efficient if theyreflect more than 60% of the extreme ultraviolet light 112.

The extreme ultraviolet reflective element production system 200includes a wafer loading and carrier handling system 202 into which thesource substrates 203 are loaded and from which the reflective elementsare unloaded. An atmospheric handling system 206 provides access to awafer handling vacuum chamber 208. The wafer loading and carrierhandling system 202 can include substrate transport boxes, loadlocks,and other components to transfer a substrate from atmosphere to vacuuminside the system. Because the EUV mask blank 204 is used to formdevices at a very small scale, the source substrates 203 and the EUVmask blank 204 are processed in a vacuum system to prevent contaminationand other defects.

The wafer handling vacuum chamber 208 can contain two vacuum chambers, afirst vacuum chamber 210 and a second vacuum chamber 212. The firstvacuum chamber 210 includes a first wafer handling system 214 and thesecond vacuum chamber 212 includes a second wafer handling system 216.Although the wafer handling vacuum chamber 208 is described with twovacuum chambers, it is understood that the system can have any number ofvacuum chambers.

The wafer handling vacuum chamber 208 can have a plurality of portsaround its periphery for attachment of various other systems. The firstvacuum chamber 210 has a degas system 218, a first physical vapordeposition system 220, a second physical vapor deposition system 222,and a pre-clean system 224. The degas system 218 is for thermallydesorbing moisture from the substrates. The pre-clean system 224 is forcleaning the surfaces of the wafers, mask blanks, mirrors, or otheroptical components.

The physical vapor deposition systems, such as the first physical vapordeposition system 220 and the second physical vapor deposition system222, can be used to form thin films of conductive materials on thesource substrates 203. For example, the physical vapor depositionsystems can include vacuum deposition system such as magnetronsputtering systems, ion sputtering systems, pulsed laser deposition,cathode arc deposition, or a combination thereof. The physical vapordeposition systems, such as the magnetron sputtering system, form thinlayers on the source substrates 203 including the layers of silicon,metals, alloys, compounds, or a combination thereof.

The physical vapor deposition system forms reflective layers, cappinglayers, and absorber layers. For example, the physical vapor depositionsystems can form layers of silicon, molybdenum, titanium oxide, titaniumdioxide, ruthenium oxide, niobium oxide, ruthenium tungsten, rutheniummolybdenum, ruthenium niobium, chromium, tantalum, nitrides, compounds,or a combination thereof. Although some compounds are described as anoxide, it is understood that the compounds can include oxides, dioxides,atomic mixtures having oxygen atoms, or a combination thereof.

The second vacuum chamber 212 has a first multi-cathode source 226, achemical vapor deposition system 228, a cure chamber 230, and anultra-smooth deposition chamber 232 connected to it. For example, thechemical vapor deposition system 228 can include a flowable chemicalvapor deposition system (FCVD), a plasma assisted chemical vapordeposition system (CVD), an aerosol assisted CVD, a hot filament CVDsystem, or a similar system. In another example, the chemical vapordeposition system 228, the cure chamber 230, and the ultra-smoothdeposition chamber 232 can be in a separate system from the extremeultraviolet reflective element production system 200.

The chemical vapor deposition system 228 can form thin films of materialon the source substrates 203. For example, the chemical vapor depositionsystem 228 can be used to form layers of materials on the sourcesubstrates 203 including mono-crystalline layers, polycrystallinelayers, amorphous layers, epitaxial layers, or a combination thereof.The chemical vapor deposition system 228 can form layers of silicon,silicon oxides, silicon oxycarbide, carbon, tungsten, silicon carbide,silicon nitride, titanium nitride, metals, alloys, and other materialssuitable for chemical vapor deposition. For example, the chemical vapordeposition system can form planarization layers.

The first wafer handling system 214 is capable of moving the sourcesubstrates 203 between the atmospheric handling system 206 and thevarious systems around the periphery of the first vacuum chamber 210 ina continuous vacuum. The second wafer handling system 216 is capable ofmoving the source substrates 203 around the second vacuum chamber 212while maintaining the source substrates 203 in a continuous vacuum. Theextreme ultraviolet reflective element production system 200 cantransfer the source substrates 203 and the EUV mask blank 204 betweenthe first wafer handling system 214, the second wafer handling system216 in a continuous vacuum.

Referring now to FIG. 4 , an embodiment of an extreme ultravioletreflective element 302 is shown. In one or more embodiments, the extremeultraviolet reflective element 302 is the EUV mask blank 204 of FIG. 3or the extreme ultraviolet mirror 205 of FIG. 3 . The EUV mask blank 204and the extreme ultraviolet mirror 205 are structures for reflecting theextreme ultraviolet light 112 of FIG. 2 . The EUV mask blank 204 can beused to form the EUV reflective mask 106 shown in FIG. 2 .

The extreme ultraviolet reflective element 302 includes a substrate 304,a multilayer stack 306 of reflective layers, and a capping layer 308. Inone or more embodiments, the extreme ultraviolet mirror 205 is used toform reflecting structures for use in the condenser 104 of FIG. 2 or theoptical reduction assembly 108 of FIG. 2 .

The extreme ultraviolet reflective element 302, which can be a EUV maskblank 204, includes the substrate 304, the multilayer stack 306 ofreflective layers, the capping layer 308, and an absorber layer 310. Theextreme ultraviolet reflective element 302 can be a EUV mask blank 204,which is used to form the reflective mask 106 of FIG. 2 by patterningthe absorber layer 310 with the layout of the circuitry required.

In the following sections, the term for the EUV mask blank 204 is usedinterchangeably with the term of the extreme ultraviolet mirror 205 forsimplicity. In one or more embodiments, the mask blank 204 includes thecomponents of the extreme ultraviolet mirror 205 with the absorber layer310 added in addition to form the mask pattern 114 of FIG. 2 .

The EUV mask blank 204 is an optically flat structure used for formingthe reflective mask 106 having the mask pattern 114. In one or moreembodiments, the reflective surface of the EUV mask blank 204 forms aflat focal plane for reflecting the incident light, such as the extremeultraviolet light 112 of FIG. 2 .

The substrate 304 is an element for providing structural support to theextreme ultraviolet reflective element 302. In one or more embodiments,the substrate 304 is made from a material having a low coefficient ofthermal expansion (CTE) to provide stability during temperature changes.In one or more embodiments, the substrate 304 has properties such asstability against mechanical cycling, thermal cycling, crystalformation, or a combination thereof. The substrate 304 according to oneor more embodiments is formed from a material such as silicon, glass,oxides, ceramics, glass ceramics, or a combination thereof.

The multilayer stack 306 is a structure that is reflective to theextreme ultraviolet light 112. The multilayer stack 306 includesalternating reflective layers of a first reflective layer 312 and asecond reflective layer 314.

The first reflective layer 312 and the second reflective layer 314 formsa reflective pair 316 of FIG. 4 . In a non-limiting embodiment, themultilayer stack 306 includes a range of 20-60 of the reflective pairs316 for a total of up to 120 reflective layers.

The first reflective layer 312 and the second reflective layer 314 canbe formed from a variety of materials. In an embodiment, the firstreflective layer 312 and the second reflective layer 314 are formed fromsilicon and molybdenum, respectively. Although the layers are shown assilicon and molybdenum, it is understood that the alternating layers canbe formed from other materials or have other internal structures.

The first reflective layer 312 and the second reflective layer 314 canhave a variety of structures. In an embodiment, both the firstreflective layer 312 and the second reflective layer 314 are formed witha single layer, multiple layers, a divided layer structure, non-uniformstructures, or a combination thereof.

Because most materials absorb light at extreme ultraviolet wavelengths,the optical elements used are reflective instead of the transmissive asused in other lithography systems. The multilayer stack 306 forms areflective structure by having alternating thin layers of materials withdifferent optical properties to create a Bragg reflector or mirror.

In an embodiment, each of the alternating layers has dissimilar opticalconstants for the extreme ultraviolet light 112. The alternating layersprovide a resonant reflectivity when the period of the thickness of thealternating layers is one half the wavelength of the extreme ultravioletlight 112. In an embodiment, for the extreme ultraviolet light 112 at awavelength of 13 nm, the alternating layers are about 6.5 nm thick. Itis understood that the sizes and dimensions provided are within normalengineering tolerances for typical elements.

The multilayer stack 306 can be formed in a variety of ways. In anembodiment, the first reflective layer 312 and the second reflectivelayer 314 are formed with magnetron sputtering, ion sputtering systems,pulsed laser deposition, cathode arc deposition, or a combinationthereof.

In an illustrative embodiment, the multilayer stack 306 is formed usinga physical vapor deposition technique, such as magnetron sputtering. Inan embodiment, the first reflective layer 312 and the second reflectivelayer 314 of the multilayer stack 306 have the characteristics of beingformed by the magnetron sputtering technique including precisethickness, low roughness, and clean interfaces between the layers. In anembodiment, the first reflective layer 312 and the second reflectivelayer 314 of the multilayer stack 306 have the characteristics of beingformed by the physical vapor deposition including precise thickness, lowroughness, and clean interfaces between the layers.

The physical dimensions of the layers of the multilayer stack 306 formedusing the physical vapor deposition technique can be preciselycontrolled to increase reflectivity. In an embodiment, the firstreflective layer 312, such as a layer of silicon, has a thickness of 4.1nm. The second reflective layer 314, such as a layer of molybdenum, hasa thickness of 2.8 nm. The thickness of the layers dictates the peakreflectivity wavelength of the extreme ultraviolet reflective element.If the thickness of the layers is incorrect, the reflectivity at thedesired wavelength 13.5 nm can be reduced.

In an embodiment, the multilayer stack 306 has a reflectivity of greaterthan 60%. In an embodiment, the multilayer stack 306 formed usingphysical vapor deposition has a reflectivity in a range of 66%-67%. Inone or more embodiments, forming the capping layer 308 over themultilayer stack 306 formed with harder materials improves reflectivity.In some embodiments, reflectivity greater than 70% is achieved using lowroughness layers, clean interfaces between layers, improved layermaterials, or a combination thereof.

In one or more embodiments, the capping layer 308 is a protective layerallowing the transmission of the extreme ultraviolet light 112. In anembodiment, the capping layer 308 is formed directly on the multilayerstack 306. In one or more embodiments, the capping layer 308 protectsthe multilayer stack 306 from contaminants and mechanical damage. In oneembodiment, the multilayer stack 306 is sensitive to contamination byoxygen, carbon, hydrocarbons, or a combination thereof. The cappinglayer 308 according to an embodiment interacts with the contaminants toneutralize them.

In one or more embodiments, the capping layer 308 is an opticallyuniform structure that is transparent to the extreme ultraviolet light112. The extreme ultraviolet light 112 passes through the capping layer308 to reflect off of the multilayer stack 306. In one or moreembodiments, the capping layer 308 has a total reflectivity loss of 1%to 2%. In one or more embodiments, each of the different materials has adifferent reflectivity loss depending on thickness, but all of them willbe in a range of 1% to 2%.

In one or more embodiments, the capping layer 308 has a smooth surface.For example, the surface of the capping layer 308 can have a roughnessof less than 0.2 nm RMS (root mean square measure). In another example,the surface of the capping layer 308 has a roughness of 0.08 nm RMS fora length in a range of 1/100 nm and 1/1 μm. The RMS roughness will varydepending on the range it is measured over. For the specific range of100 nm to 1 micron that roughness is 0.08 nm or less. Over a largerrange the roughness will be higher.

The capping layer 308 can be formed in a variety of methods. In anembodiment, the capping layer 308 is formed on or directly on themultilayer stack 306 with magnetron sputtering, ion sputtering systems,ion beam deposition, electron beam evaporation, radio frequency (RF)sputtering, atomic layer deposition (ALD), pulsed laser deposition,cathode arc deposition, or a combination thereof. In one or moreembodiments, the capping layer 308 has the physical characteristics ofbeing formed by the magnetron sputtering technique including precisethickness, low roughness, and clean interfaces between the layers. In anembodiment, the capping layer 308 has the physical characteristics ofbeing formed by the physical vapor deposition including precisethickness, low roughness, and clean interfaces between the layers.

In one or more embodiments, the capping layer 308 is formed from avariety of materials having a hardness sufficient to resist erosionduring cleaning. In one embodiment, ruthenium is used as a capping layermaterial because it is a good etch stop and is relatively inert underthe operating conditions. However, it is understood that other materialscan be used to form the capping layer 308. In specific embodiments, thecapping layer 308 has a thickness of in a range of 2.5 and 5.0 nm.

In one or more embodiments, the absorber layer 310 is a layer thatabsorbs the extreme ultraviolet light 112. In an embodiment, theabsorber layer 310 is used to form the pattern on the reflective mask106 by providing areas that do not reflect the extreme ultraviolet light112. The absorber layer 310, according to one or more embodiments,comprises a material having a high absorption coefficient for aparticular frequency of the extreme ultraviolet light 112, such as about13.5 nm. In an embodiment, the absorber layer 310 is formed directly onthe capping layer 308, and the absorber layer 310 is etched using aphotolithography process to form the pattern of the reflective mask 106.

According to one or more embodiments, the extreme ultraviolet reflectiveelement 302, such as the extreme ultraviolet mirror 205, is formed withthe substrate 304, the multilayer stack 306, and the capping layer 308.The extreme ultraviolet mirror 205 has an optically flat surface and canefficiently and uniformly reflect the extreme ultraviolet light 112.

According to one or more embodiments, the extreme ultraviolet reflectiveelement 302, such as the EUV mask blank 204, is formed with thesubstrate 304, the multilayer stack 306, the capping layer 308, and theabsorber layer 310. The mask blank 204 has an optically flat surface andcan efficiently and uniformly reflect the extreme ultraviolet light 112.In an embodiment, the mask pattern 114 is formed with the absorber layer310 of the mask blank 204.

According to one or more embodiments, forming the absorber layer 310over the capping layer 308 increases reliability of the reflective mask106. The capping layer 308 acts as an etch stop layer for the absorberlayer 310. When the mask pattern 114 of FIG. 2 is etched into theabsorber layer 310, the capping layer 308 beneath the absorber layer 310stops the etching action to protect the multilayer stack 306.

Referring now to FIG. 5 , an extreme ultraviolet (EUV) mask blank 400 isshown as comprising a substrate 414, a multilayer stack of reflectivelayers 412 on the substrate 414, the multilayer stack of reflectivelayers 412 including a plurality of reflective layer pairs. The EUV maskblank 400 further includes a capping layer 422 on the multilayer stackof reflective layers 412, and there is a multilayer stack 420 ofabsorber layers 420 on the capping layer 422. The multilayer stack 420of absorber layers including a plurality of absorber layer pairs 420 a,420 b, 420 c, 420 d, 420 e, 420 f, each pair (420 a/420 b, 420 c/420 d,420 e/420 f) comprising two different absorber materials havingextinction coefficient (k) values that are different and index ofrefraction values (n) that are different. For example, absorber layer420 a is made from a material that has an extinction coefficient value(k) that is different from the extinction coefficient value (k) of thematerial that forms absorber layer 420 b. Likewise, absorber layer 420 cis made from a material that has an extinction coefficient value (k)that is different from the extinction coefficient value (k) of thematerial that forms absorber layer 420 d, and absorber layer 420 e ismade from a material that has an extinction coefficient value (k) thatis different from the extinction coefficient value (k) of the materialthat forms absorber layer 420 f. Furthermore, absorber layer 420 a ismade from a material that has an index of refraction values (n) that isdifferent from the index of refraction values (n) of the material thatforms absorber layer 420 b. Likewise, absorber layer 420 c is made froma material that has an index of refraction values (n) that is differentfrom the index of refraction values (n) of the material that formsabsorber layer 420 d, and absorber layer 420 e is made from a materialthat has an index of refraction values (n) that is different from theindex of refraction values (n) of the material that forms absorber layer420 f.

In one embodiment, the extreme ultraviolet mask blank 400 includes theplurality of reflective layers 412 are selected from molybdenum (Mo)containing material and silicon (Si) containing material, for example,molybdenum (Mo) and silicon (Si). The absorber materials that are usedto form the absorber layers 420 a, 420 b, 420 c, 420 d, 420 e and 420 fare selected from the group consisting of platinum (Pt), zinc (Zn), gold(Au), nickel oxide (NiO), silver oxide (Ag₂O), iridium (Ir), iron (Fe),tin dioxide (SnO₂), cobalt (Co), chromium nickel alloys, Ni₈Cr₂, tinoxide (SnO), copper (Cu), silver (Ag), actinium (Ac), tellurium (Te),caesium iodide (CsI), tin (Sn), zinc telluride (ZnTe), antimony (Sb),tantalum (Ta), tantalum nitride (TaN), tantalum nitride oxide (TaNO),chromium (Cr), chromium nitride (CrN) and tantalum borate (TaBO).

In one or more embodiments, wherein the absorber layer pairs 420 a/420b, 420 c/420 d, 420 e/420 f comprise a first layer (420 a, 420 c, 420 e)including an absorber material selected from the group consisting oftantalum (Ta), tantalum nitride (TaN), tantalum nitride oxide (TaNO),tantalum borate (TaBO) and a second layer (420 b, 420 d, 420 f)including an absorber material selected from the group consisting ofplatinum (Pt), zinc (Zn), gold (Au), nickel oxide (NiO), silver oxide(Ag₂O), iridium (Ir), iron (Fe), tin dioxide (SnO₂), cobalt (Co),chromium nickel alloys, in particular Ni₈Cr₂, tin oxide (SnO), copper(Cu), silver (Ag), actinium (Ac), tellurium (Te), caesium iodide (CsI),tin (Sn), zinc telluride (ZnTe), chromium (Cr), chromium nitride (CrN)and antimony (Sb). In specific embodiments, the absorber layer pairscomprise a first layer (420 a, 420 c, 420 e) including an absorbermaterial selected from tantalum nitride (TaN) and a second layer (420 b,420 d, 420 f) including an absorber material selected from nickel (Ni).

According to one or more embodiments, the absorber layer pairs comprisea first layer (420 a, 420 c, 420 e) and a second absorber layer (420 b,420 d, 420 f) each of the first absorber layers (420 a, 420 c, 420 e)and second absorber layer (420 b, 420 d, 420 f) have a thickness in arange of 0.1 nm and 10 nm, for example in a range of 1 nm and 5 nm, orin a range of 1 nm and 3 nm. In one or more specific embodiments, thethickness of the first layer 420 a is 0.5 nm, 0.6 nm, 0.7 nm, 0.8 nm,0.9 nm, 1 nm, 1.1 nm, 1.2 nm, 1.3 nm, 1.4 nm, 1.5 nm, 1.6 nm, 1.7 nm,1.8 nm, 1.9 nm, 2 nm, 2.1 nm, 2.2 nm, 2.3 nm, 2.4 nm, 2.5 nm, 2.6 nm,2.7 nm, 2.8 nm, 2.9 nm, 3 nm, 3.1 nm, 3.2 nm, 3.3 nm, 3.4 nm, 3.5 nm,3.6 nm, 3.7 nm, 3.8 nm, 3.9 nm, 4 nm, 4.1 nm, 4.2 nm, 4.3 nm, 4.4 nm,4.5 nm, 4.6 nm, 4.7 nm, 4.8 nm, 4.9 nm, and 5 nm. In one or moreembodiments, the thickness of the first absorber layer and secondabsorber layer of each pair is the same different. For example, thefirst absorber layer and second absorber layer have a thickness suchthat there is a ratio of the first absorber layer thickness to secondabsorber layer thickness of 1:1, 1.5:1, 2:1, 2.5:1, 3:1, 3.5:1, 4:1,4.5:1, 5:1, 6:1, 7:1, 8:1, 9:1, 10:1, 11:1, 12:1, 13:1, 14:1, 15:1,16:1, 17:1, 18:1, 19:1, or 20:1, which results in the first absorberlayer having a thickness that is equal to greater than the secondabsorber layer thickness in each pair. Alternatively, the first absorberlayer and second absorber layer have a thickness such that there is aratio of the second absorber layer thickness to first absorber layerthickness of 1.5:1, 2:1, 2.5:1, 3:1, 3.5:1, 4:1, 4.5:1, 5:1, 6:1, 7:1,8:1, 9:1, 10:1, 11:1, 12:1, 13:1, 14:1, 15:1, 16:1, 17:1, 18:1, 19:1, or20:1 which results in the second absorber layer having a thickness thatis equal to greater than the first absorber layer thickness in eachpair.

According to one or more embodiments, the different absorber materialsand thickness of the absorber layers are selected so that extremeultraviolet light is absorbed due to absorbance and due to a phasechange caused by destructive interference with light reflected from themultilayer stack of reflective layers. While the embodiment shown inFIG. shows three absorber layer pairs, 420 a/420 b, 420 c/420 d and 420e/420 f, the claims should not be limited to a particular number ofabsorber layer pairs. According to one or more embodiments, the EUV maskblank 400 can include in a range of 5 and 60 absorber layer pairs or ina range of 10 and 40 absorber layer pairs.

According to one or more embodiments, the absorber layers have athickness which provides less than 2% reflectivity and other etchproperties. A supply gas can be used to further modify the materialproperties of the absorber layers, for example, nitrogen (N₂) gas can beused to form nitrides of the materials provided above. The multilayerstack of absorber layers according to one or more embodiments is arepetitive pattern of individual thickness of different materials sothat the EUV light not only gets absorbed due to absorbance but by thephase change caused by multilayer absorber stack, which willdestructively interfere with light from multilayer stack of reflectivematerials beneath to provide better contrast.

For example, consider a first case, an absorber stack of 10 nm Ni with15 nm TaN on 40 ML of Mo and Si. The absorber stack will absorb EUV at13.5 nm based on n and k of Ni and TaN. In a second case according to anembodiment, 5 bilayers of Ni and TaN of thickness 2 and 3 nm on top of40 ML of Mo and Si can be made. In the second case, the light is notonly absorbed by total thickness of 10 nm of Ni and 15 nm of TaN butadditionally provides phase change of light which destructivelyinterferes with reflected light from 40 ML of Mo and Si mirror providingenhanced contrast. Therefore, the second case stack will provide morethan 50% improvement in the reflectivity loss. A gamma, which is a ratioof thickness of Ni with TaN, individual layer thickness and number ofmultilayers can be further optimized to provide even more contrast. FIG.6 is a reflectivity curve for the first case and FIG. 7 is areflectivity curve for the second case.

Another aspect of the disclosure pertains to a method of manufacturingan extreme ultraviolet (EUV) mask blank comprising providing asubstrate, forming a multilayer stack of reflective layers on thesubstrate, the multilayer stack including a plurality of reflectivelayer pairs, forming a capping layer on the multilayer stack ofreflective layers, and forming a multilayer stack of absorber layers onthe capping layer, the multilayer stack of absorber layers including aplurality of absorber layer pairs, each pair comprising two differentabsorber materials having extinction coefficient (k) values that aredifferent and index of refraction values (n) that are different. The EUVmask blank can have any of the characteristics of the embodimentsdescribed above with respect to FIG. 4 and FIG. 5 , and the method canbe performed in the system described with respect to FIG. 3 .

Thus, in an embodiment, the plurality of reflective layers are selectedfrom molybdenum (Mo) containing material and silicon (Si) containingmaterial and the absorber layers are made from materials selected fromthe group consisting of platinum (Pt), zinc (Zn), gold (Au), nickeloxide (NiO), silver oxide (Ag₂O), iridium (Ir), iron (Fe), tin dioxide(SnO₂), cobalt (Co), chromium nickel alloys, Ni₈Cr₂, tin oxide (SnO),copper (Cu), silver (Ag), actinium (Ac), tellurium (Te), caesium iodide(CsI), tin (Sn), zinc telluride (ZnTe), antimony (Sb), tantalum (Ta),tantalum nitride (TaN), tantalum nitride oxide (TaNO), tantalum borate(TaBO). Alternatively, in an embodiment, the absorber layer pairscomprise a first layer including an made from a material selected fromthe group consisting of tantalum (Ta), tantalum nitride (TaN), tantalumnitride oxide (TaNO), tantalum borate (TaBO) and a second layer madefrom a material selected from the group consisting of platinum (Pt),zinc (Zn), gold (Au), nickel oxide (NiO), silver oxide (Ag₂O), iridium(Ir), iron (Fe), tin dioxide (SnO₂), cobalt (Co), chromium nickelalloys, in particular Ni₈Cr₂, tin oxide (SnO), copper (Cu), silver (Ag),actinium (Ac), tellurium (Te), caesium iodide (CsI), tin (Sn), zinctelluride (ZnTe), chromium (Cr), chromium nitride (CrN) and antimony(Sb). In a specific embodiment, an absorber layer pair comprises a firstlayer including an absorber material selected from tantalum nitride(TaN) and a second layer selected from nickel (Ni).

In another specific method embodiment, the different absorber layers areformed in a physical vapor deposition chamber having a first cathodecomprising a first absorber material and a second cathode comprising asecond absorber material. Referring now to FIG. 8 an upper portion of amulti-cathode source chamber 500 is shown in accordance with anembodiment. The first multi-cathode chamber 500 includes a basestructure 501 with a cylindrical body portion 502 capped by a topadapter 504. The top adapter 504 has provisions for a number of cathodesources, such as cathode sources 506, 508, 510, 512, and 514, positionedaround the top adapter 204.

The multi-cathode source chamber 500 can be part of the system shown inFIG. 3 . In an embodiment, an extreme ultraviolet (EUV) mask blankproduction system comprises a substrate handling vacuum chamber forcreating a vacuum, a substrate handling platform, in the vacuum, fortransporting a substrate loaded in the substrate handling vacuumchamber, and multiple sub-chambers, accessed by the substrate handlingplatform, for forming an EUV mask blank, including a multilayer stack ofreflective layers on the substrate, the multilayer stack including aplurality of reflective layer pairs, a capping layer on the multilayerstack reflective layers, and a multilayer stack of absorber layers onthe capping layer, the multilayer stack of absorber layers including aplurality of absorber layer pairs, each pair comprising two differentabsorber materials having extinction coefficient (k) values that aredifferent and index of refraction values (n) that are different. Thesystem can be used to make the EUV mask blanks shown with respect toFIG. 4 or FIG. 5 and have any of the properties described with respectto the EUV mask blanks described with respect to FIG. 4 or FIG. 5 above.

Reference throughout this specification to “one embodiment,” “certainembodiments,” “one or more embodiments” or “an embodiment” means that aparticular feature, structure, material, or characteristic described inconnection with the embodiment is included in at least one embodiment ofthe disclosure. Thus, the appearances of the phrases such as “in one ormore embodiments,” “in certain embodiments,” “in one embodiment” or “inan embodiment” in various places throughout this specification are notnecessarily referring to the same embodiment of the disclosure.Furthermore, the particular features, structures, materials, orcharacteristics may be combined in any suitable manner in one or moreembodiments.

Although the disclosure herein has been described with reference toparticular embodiments, it is to be understood that these embodimentsare merely illustrative of the principles and applications of thepresent disclosure. It will be apparent to those skilled in the art thatvarious modifications and variations can be made to the method andapparatus of the present disclosure without departing from the spiritand scope of the disclosure. Thus, it is intended that the presentdisclosure include modifications and variations that are within thescope of the appended claims and their equivalents.

What is claimed is:
 1. A method of manufacturing an extreme ultraviolet(EUV) mask blank comprising: forming a multilayer stack of reflectivelayers on a substrate, the multilayer stack of reflective layersincluding a plurality of reflective layer pairs; forming a capping layeron the multilayer stack of reflective layers; and forming a multilayerstack of absorber layers on the capping layer, the multilayer stack ofabsorber layers including a plurality of absorber layer pairs, each paircomprising two different absorber materials having extinctioncoefficient (k) values that are different and index of refraction values(n) that are different, wherein the absorber layer pairs comprise afirst layer including an absorber material selected from tantalumnitride (TaN) and tantalum nitride oxide (TaNO), and a second layerincluding an absorber material selected from the group consisting ofzinc (Zn), iron (Fe), cobalt (Co), chromium-nickel alloys, Ni₈Cr₁₂,copper (Cu) and zinc telluride (ZnTe).
 2. The method of claim 1, whereinthe first layer includes tantalum nitride (TaN).
 3. The method of claim1, wherein the first layer includes tantalum nitride oxide (TaNO). 4.The method of claim 1, wherein the second layer includes zinc (Zn). 5.The method of claim 1, wherein the second layer is selected from thegroup consisting of chromium-nickel alloys and Ni₈Cr₁₂.
 6. The method ofclaim 1, wherein the second layer includes iron (Fe).
 7. The method ofclaim 1, wherein the second layer includes cobalt (Co).
 8. The method ofclaim 1, wherein the second layer includes copper (Cu).
 9. The method ofclaim 1, wherein the second layer includes zinc telluride (ZnTe). 10.The method of claim 1, wherein the method comprises forming a range offrom 5 to 60 absorber layer pairs.
 11. An extreme ultraviolet (EUV) maskblank comprising: a substrate; a multilayer stack of reflective layerson the substrate, the multilayer stack of reflective layers including aplurality of reflective layers including reflective layer pairs; acapping layer on the multilayer stack of reflective layers; and amultilayer stack of absorber layers on the capping layer, the multilayerstack of absorber layers including a plurality of absorber layer pairs,each pair comprising two different absorber materials having extinctioncoefficient (k) values that are different and index of refraction values(n) that are different, wherein the absorber layer pairs comprise afirst layer including an absorber material selected from tantalumnitride (TaN) and tantalum nitride oxide (TaNO), and a second layerincluding an absorber material selected from the group consisting ofzinc (Zn), iron (Fe), cobalt (Co), chromium-nickel alloys, Ni₈Cr₁₂,copper (Cu) and zinc telluride (ZnTe).
 12. The EUV mask blank of claim11, wherein the first layer includes tantalum nitride (TaN).
 13. The EUVmask blank of claim 11, wherein the first layer includes tantalumnitride oxide (TaNO).
 14. The EUV mask blank of claim 1, wherein thesecond layer includes zinc (Zn).
 15. The EUV mask blank of claim 11,wherein the second layer is selected from the group consisting ofchromium-nickel alloys and Ni₈Cr₁₂.
 16. The EUV mask blank of claim 11,wherein the second layer includes iron (Fe).
 17. The EUV mask blank ofclaim 11, wherein the second layer includes cobalt (Co).
 18. The EUVmask blank of claim 1, wherein the second layer includes copper (Cu).19. The EUV mask blank of claim 11, wherein the second layer includeszinc telluride (ZnTe).
 20. The EUV mask blank of claim 11, comprising arange of from 5 to 60 absorber layer pairs.